Method of manufacturing a semiconductor device

ABSTRACT

A heat treatment for diffusing impurity ions implanted into a silicon layer is performed at a heat treatment temperature which is less than an aggregation temperature of the silicon layer. A thermal aggregation of the silicon layer can be inhibited, thereby reducing a silicon deficiency of the silicon layer.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a method of manufacturing a semiconductor device which is formed in silicon layer located on an insulating layer, or on a silicon-on insulator (SOI) substrate.

[0003] The present application claims priority under 35 U.S.C. §119 to Japanese Patent Application No. 2001-160597, filed May 29, 2001, which is herein incorporated by reference in its entirely for all purposes.

[0004] 2. Description of the related art

[0005] A field effect transistors are now typically formed on the SOI substrate (which is called an SOI-FET) instead of the more conventional bulk semiconductor substrate. The SOI-FET is formed in the thin silicon layer (the SOI layer) which is formed on the insulating layer of the SOI substrate. Since a junction capacitance is reduced by such a structure, the SOI-FET can operate at a high-speed. Particularly, a fully depleted SOI-FET formed in the SOI layer is known as a low-power device which has a small parasitic capacitance and a sub-threshold swing which is smaller than that of the conventional bulk semiconductor substrate. The fully depleted transistor has a depletion layer that expand to the bottom surfaces of a source region and a drain region, when a voltage is supplied to a gate electrode thereof. Since an expansion of the depleted layer of the fully depleted SOI-FET is defined by a thickness of the. SOI layer, a short channel effect can be inhibited. Thus, the thickness of the SOI layer is reduced to achieve the fully depleted operation of the SOI-FET.

[0006] Such a fully depleted SOI-FET having the source and drain regions in the SOI layer is constructed with an island shaped full isolation structure by performing an element isolation process, for example a local oxidation of silicon process (a LOCOS process). A region between the source and drain regions is called a body region. The body region is basically depleted when the fully depleted SOI-FET is operating.

[0007] Since a thickness of a channel depleted layer is determined in accordance with the thickness of the SOI layer, it is necessary reduce the thickness of the thinner SOI layer. When an extremely thin SOI layer (e.g. 10 nm) is formed, defects may arise due to a heat treatment process which is performed at a temperature of 900° C. or more. The heat treatment may cause a void to be opened in the SOI layer due to a thermal aggregation (also called a thermal agglomeration), and an upper surface of the insulating layer under the SOI layer might be exposed. Such a void generated by the thermal aggregation is disclosed in the magazine article of the lecture presentation of the 47^(th) Applied Physics Association, pp. 884, 30p-YK-9, “Initial Stage of Thermal Agglomeration of an Ultrathin SOI”, published in March, 2000. If a subsequent dry etching process forming a contact hole were performed on an SOI substrate having such a void, the void might extend through the insulating layer and be formed in the conductive substrate under the insulating layer. If such a void were formed at the edge of the SOI-FET, the drive current of the SOI-FET might be reduced, since a parasitic resistance of the source and drain regions would be increased so as to increase a resistance between the source and drain regions.

[0008] Further more, if a contact plug consisting of a metal material is formed in the contact hole, and a wiring layer connecting the contact plug is formed over the SOI substrate, since the contact plug is also formed in the void, the source and drain regions and the silicon substrate might be electrically shorted.

[0009] FIGS. 6(a) through 6(c) and 7(a) through 7(c) are cross-sectional views showing a conventional method of manufacturing a semiconductor device. An SOI substrate 101 includes a silicon substrate 101 a, an embedded oxide layer 101 b and a thin silicon layer 101 c (an SOI layer 101 c). As shown in FIG. 6(a), field oxide regions 102 and highly doped impurity regions 108 a and 108 b are formed in the SOI layer 101 c, and gate electrodes 105 a and 105 b and side walls 107 a and 107 b are formed over the SOI substrate 101. The highly doped impurity layers 108 a and 108 b are formed by an implantation of impurity ions.

[0010] Then, a heat treatment is performed to activate the ion-implanted impurities at a high temperature. At this time, as shown in FIG. 6(b), the highly doped impurity layers 108 a and 108 b gradually aggregates since the temperature of the heat treatment is equal to or more than an aggregation temperature of the SOI layer 101 c consisting of silicon. As such, when the SOI layer is ultra-thin, upper surfaces R of the embedded oxide layer 101 b become partly exposed.

[0011] Next, as shown in FIG. 6(c), refractory metal silicide layers 109 a and 109 b are formed by a conventional silicide process.

[0012] Next, as shown in FIG. 7(a), an interlayer insulating layer 110 is formed over the SOI substrate 101.

[0013] Next, as shown in FIG. 7(b), contact holes 111 a and 111 b are formed by an anisotropic etching, for example, a dry etching such as a reactive ion etching (RIE). At this time, since the embedded oxide layer 101 b is partly exposed, a void 113 is formed extending through the embedded oxide layer 101 b and reaching an upper surface of the silicon substrate 101 a. As a result, since a parasitic resistance of the highly doped impurity layers 108 a and 108 b increases so as to increase a resistance between the highly doped impurity layers 108 a and 108 b, and the drive current of the SOI-FET is reduced.

[0014] Next, as shown in FIG. 7(c), a contact plug 112 a consisting of a metal material is formed in the contact holes 111 a and 111 b, and a wiring layer 112 b connecting the contact plug 112 a is formed over the SOI substrate 101. At this time, since the contact plug 112 a is also formed in the void 113, the highly doped impurity layer 108 a and the silicon substrate 101 a are electrically shorted.

[0015] The conventional SOI-MOSFET is disclosed in an article of Proceeding 1995 IEEE International SOI Conference, October 1995, pp.116-117, “Characteristics of Submicrometer LOCOS Isolation”, published on October, 1995.

SUMMARY OF THE INVENTION

[0016] In a method of manufacturing a semiconductor device according to the present invention, a substrate is provided which includes an insulating layer having an upper surface and a silicon layer extending over the upper surface of the insulating layer, a field insulating region is formed in the silicon layer, an impurity region is formed which is surrounded by the field insulating region, a gate electrode is formed over the silicon layer, and the silicon layer is heat treated at a heat treatment temperature that is less than an aggregation temperature of the silicon layer.

[0017] According to the present invention, a thermal aggregation of a silicon layer can be inhibited. Therefore, a silicon deficiency of the silicon layer caused by the thermal aggregation of the silicon layer can be inhibited.

[0018] The above and further novel features of the invention will more fully apparent from the following detailed description, appended claims and accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] While the specification concludes with claims particularly pointing out and distinctly claiming the subject matter which is regarded as the invention, it is believed that the invention, the objects and features of the invention and further objects, features and advantages thereof will be better understood from the following description taken in connection with the accompanying drawings in which:

[0020] FIGS. 1(a) and 1(b) are cross-sectional views showing a method of manufacturing a semiconductor device according to a first preferred embodiment of the present invention;

[0021]FIG. 2 is an explanatory diagram showing an experimental result of a heat treatment according to the first preferred embodiment of the present invention;

[0022] FIGS. 3(a) through 3(e) and 4(a) through 4(c) are cross-sectional views showing a method of manufacturing a semiconductor device according to a second preferred embodiment of the present invention;

[0023] FIGS. 5(a) through 5(e) are cross-sectional views showing a method of manufacturing a semiconductor device according to a third preferred embodiment of the present invention; and

[0024] FIGS. 6(a) through 6(c) and 7(a) through 7(c) are cross-sectional views showing a conventional method of manufacturing a semiconductor device.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0025] Preferred embodiments of the present invention will hereinafter be described in detail with reference to the accompanying drawings. The drawings used for this description typically illustrate major characteristic parts in order that the present invention will be easily understood.

[0026] FIGS. 1(a) and 1(b) are cross-sectional views showing a method of manufacturing a semiconductor device according to a first preferred embodiment of the present invention. An SOI substrate 101 includes a silicon substrate 101 a, an embedded oxide layer 101 b and a thin silicon layer 101 c (an SOI layer 101 c). As shown in FIG. 1(a), a field oxide region 102 and a highly doped impurity region 108 are formed in the SOI layer 101 c, and a gate electrode 105 and a side wall 107 are formed over the SOI substrate 101. The highly doped impurity region 108 is formed by an implantation of impurity ions. Then, a heat treatment is performed to activate the ion-implanted impurities. At this time, it is necessary to understand a start temperature (an aggregation temperature) of the thermal aggregation of the SOI layer 108, so as to inhibit the thermal aggregation of the SOI layer 108.

[0027]FIG. 2 is an explanatory diagram showing an experimental result of a heat treatment according to the first preferred embodiment of the present invention. In this experiment, the heat treatment is performed for 5 minutes in a hydrogen atmosphere under 266 Pa pressure. FIG. 2 shows a relationship between a temperature (° C.) of the heat treatment (in a vertical axis) and a thickness (nm) of the SOI layer 108 (in a horizontal axis). In particular, an evaluation was made as to whether an aggregation of the SOI layer 108 was generated at each of the various heat treatment temperatures and thicknesses of the SOI layer. In FIG. 2, white triangles indicate that the SOI layer 108 had aggregated, and white circles indicates that the SOI layer 108 had not aggregated.

[0028] When the aggregation temperature and the thickness of SOI layer 108 are T and t, respectively, the aggregation temperature T can be represented as a function of the thickness t. Specifically, the relationship between the aggregation temperature T and the thickness t of the SOI layer 108 can be indicated as the following equation (1).

T=(10t+530) ° C./nm   (1)

[0029] For example, when the thickness t of the SOI layer 108 is 30 nm, the aggregation temperature T of the SOI layer 108 a is 830° C. Also, when the thickness t of the SOI layer 108 is 10 nm, the aggregation temperature T of the SOI layer 108 is 630° C.

[0030] In the first preferred embodiment, the heat treatment is performed at a temperature which is less than the aggregation temperature of the SOI layer 108 a. Therefore, as shown in FIG. 1(b), the ion-implanted impurities into the SOI layer 108 are activated without the aggregation of the SOI layer 108, due to the heat treatment which is performed at the temperature of less than the aggregation temperature of the SOI layer 108. Specifically, an upper surface of the embedded oxide layer 101 b is not exposed as shown in FIG. 5(b) in the prior art.

[0031] According to the first preferred embodiment of the present invention, since the heat treatment is performed at a temperature which is less than the aggregation temperature of the SOI layer 108, the aggregation of the SOI layer 108 can be inhibited. Therefore, the method of the first preferred embodiment can inhibit a silicon deficiency of the SOI layer 108.

[0032] FIGS. 3(a) through 3(e) and 4(a) through 4(c) are cross-sectional views showing the method of manufacturing a semiconductor device according to a second preferred embodiment of the present invention. In this embodiment, a method for manufacturing a fully depleted SOI-FET will be described. An SOI substrate 11 includes a silicon substrate 11 a, an embedded oxide layer 11 b and a thin silicon layer 11 c (an SOI layer 11 c). As shown in FIG. 3(a), field oxide regions 12 and circuit regions 13 a and 13 b are formed over the SOI substrate 11 using a LOCOS process. An N type impurity ion (e.g., Boron) is implanted into the circuit region 13 a, and a P type impurity ion (e.g., Phosphorus) is implanted into the circuit region 13 b. Then, a heat treatment is performed to activate the impurity ions (Boron and Phosphorus).

[0033] Next, as shown in FIG. 3(b), an oxide layer 14 is formed over the SOI substrate 11 using an electric furnace, and a poly-silicon layer 16 is formed on the oxide layer 14 using a CVD apparatus.

[0034] Next, as shown in FIG. 3(c), gate electrodes 15 a and 15 b are formed using a photolithography process and an anisotropic etching of the poly-silicon layer 16 using a dry etching process (e.g., RIE: reactive ion etching).

[0035] Next, as shown in FIG. 3(d), side walls 17 a and 17 b consisting of an insulating material (e.g., silicon oxide (SiO₂) or silicon nitride (SiN₄)) are formed using the CVD process and the anisotropic etching. Then, an As ion is implanted into a source-drain region of the circuit region 13 a, after a resist layer 40 is formed over the circuit region 13 b having the gate electrode 15 b. As a result, a highly doped impurity layer 18 a is obtained. Then, the resist layer 40 is removed.

[0036] Next, as shown in FIG. 3(e), a BF₂ ion is implanted into a source-drain region of the circuit region 13 b, after a resist layer 41 is formed over the circuit region 13 b having the gate electrode 15 b. As a result, a highly doped impurity layer 18 b is obtained. Then, the resist layer 41 is removed.

[0037] As a general observation, a thin chemical oxide layer may be formed on the SOI layer when a cleaning process of the SOI substrate is performed before the heat treatment process. However, since such a thin chemical oxide layer is deoxidized at a temperature of more than 800° C. due to a silicon (Si), and then sublimes as a silicon oxide (SiO2), a clean upper surface of the SOI layer is exposed. Such a deoxidization of the thin chemical oxide layer is disclosed in the magazine article of the JAPANESE JOURNAL OF APPLIED PHYSICS, VOL. 29, NO. 6, JUNE, 1990, pp. 1004-1008, “Thermal Desorption from Si (111) Surfaces with Native Oxide Formed During Chemical Treatments”.

[0038] Therefore, in the second preferred embodiment, as shown in FIG. 4(a), a protection layer 30 (e.g., silicon oxide (SiO₂) or silicon nitride (SiN₄)) is formed over the SOI substrate 11. At this time, a thickness of the protection layer 30 is equal to or more than 1 nm. Then, a heat treatment is performed to activate the ion-implanted impurities at a temperature of 1000° C. in a nitride atmosphere using a rapid thermal anneal (RTA). At this time, since upper surfaces of the highly doped impurity layers 18 a and 18 b which are the SOI layer are covered and protected by the protection layer 30, the highly doped impurity layers 18 a and 18 b which are the SOI layer do not aggregate. Therefore, an upper surface of the embedded oxide layer 11 b locating at the circuit regions 13 a and 13 b does not exposes.

[0039] Next, as shown in FIG. 4(b), refractory metal silicide layers 19 a and 19 b are formed in the highly doped impurity layers 18 a and 18 b, respectively, by a silicide process after the protection layer 30 is removed.

[0040] Next, as shown in FIG. 4(c), an interlayer insulating layer 20 is formed over the SOI substrate 11 by a CVD process. Then, contact holes 21 a and 21 b are formed in the interlayer insulating layer 20, by an anisotropic etching of the interlayer insulating layer 20 using a dry etching process (e.g., RIE: reactive ion etching). Then, a contact plug 22 a consisting of a refractory metal material (e.g., tungsten (W)) is formed in the contact holes 21 a and 21 b, and a wiring layer 22 b connecting the contact plug is formed over the SOI substrate 11.

[0041] According to the second preferred embodiment of the present invention, since the protection layer 30 is formed over upper surfaces of the highly doped impurity layers 18 a and 18 b which are the SOI layer, before the heat treatment which activates the ion-implanted impurities is preformed, the aggregation of the SOI layer 108 can be inhibited. Therefore, the method of the first preferred embodiment can inhibit a silicon deficiency of the SOI layer 108. Further, since the heat treatment can be performed at a high temperature, a crystal deficiency remaining to the highly doped impurity layers 18 a and 18 b can be effectively recovered. Therefore, the second preferred embodiment can form the SOI-FET having small parasitic leakage.

[0042] While the second preferred embodiment of the present invention presents an example in which the protection layer is formed before the heat treatment is performed, the invention is not limited to this, and may instead be formed in the early heat treatment stages before a temperature of the heat treatment reaches the aggregation temperature of the SOI layer. Further, a thermal oxide layer which has a thickness which is equal to or more than 1 nm may be formed over the upper surface of the SOI layer as a protection layer, by introducing a particle of oxide gas in the early heat treatment stage. As a result, since the protection layer is formed during the heat treatment process, a total manufacturing time can be shortened.

[0043] FIGS. 5(a) through 5(e) are cross-sectional views showing a method of manufacturing a semiconductor device according to a third preferred embodiment of the present invention. The third preferred embodiment will be described as an example of a method of manufacturing of a semiconductor device such that an the SOI-FET and a single-electron memory (the quantum effect device) are simultaneously formed over an SOI substrate.

[0044] An SOI substrate 51 includes a silicon substrate 51 a, an embedded oxide region 51 b and a thin silicon layer 51 c (an SOI layer 11 c). As shown in FIG. 5(a), field oxide regions 52 and circuit regions 53 a and 53 b are formed over the SOI substrate 51 using a LOCOS process. At this time, the SOI-FET is formed in the circuit region 53 a, and the single-electron memory is formed in the circuit region 53 b. Then, after a resist pattern is formed on the circuit region 53 b, an N type impurity ion (e.g., Boron) is implanted into the circuit region 53 a, or a P type impurity ion (e.g., Phosphorus) is implanted into the circuit region 53 a, depending on the conductive type of the SOI-FET. Then, a heat treatment is performed to activate the impurity ion (Boron or Phosphorus).

[0045] Next, as shown in FIG. 5(b), similar to the second preferred embodiment, an oxide region 54, a gate electrode 55 and a side wall 57 are formed in the circuit region 53 a. The oxide region 54 is formed using an electric furnace. The gate electrode 55 which may be a poly-silicon, for example, is formed using a CVD process and an anisotropic etching (e.g., RIE: reactive ion etching). The side wall 57 consisting of an insulating material (e.g., silicon oxide (SiO₂) or silicon nitride (SiN₄)) is formed using the CVD process and the anisotropic etching. Then, as shown in FIG. 5(b), impurity ion is implanted into the source-drain region (the circuit region 53 a) to form a highly doped impurity layer 58, using the resist layer 60 as a mask.

[0046] Next, an insulating layer which may be a silicon oxide (SiO₂) or a silicon nitride (SiN₄), for example, is formed over of the SOI substrate 51 which includes both circuit regions 53 a and 53 b, after the resist layer 60 is removed. A thickness of the insulating layer is more than 1 nm. Then, as shown in FIG. 5(c), a protection layer 70 is formed in the circuit region 53 a, and a plurality of insulating patterns 71 are formed in the circuit region 53 b, due to a patterning of the insulating layer by an etching.

[0047] Next, a heat treatment is performed to activate the ion-implanted impurities at a temperature of more than 800° C. in a nitride atmosphere using a rapid thermal anneal (RTA). As a result, as shown in FIG. 5(d), a plurality of quantum dots 72 which have a silicon island structure are formed in the circuit region 53 b, due to a thermal aggregation of the SOI layer 51 b of the circuit region 53 b. However, since the SOI layer 51 b of the circuit region 53 a is protected from the high temperature of the heat treatment by the protection layer 70, the SOI layer 51 b of the circuit region 53 a does not aggregate.

[0048] Next, as shown in FIG. 5(e), a refractory metal silicide layer 59 is formed in the highly doped impurity layer 58 by a silicide process after the protect layer 70 and the plurality of insulating patterns 71 are removed. The subsequent processes of the manufacturing method of the third preferred embodiment are the same of the second preferred embodiment.

[0049] According to the third preferred embodiment of the present invention, since the heat treatment is performed after the circuit region 53 a of the semiconductor substrate 51 is covered by the protection layer 70 and the plurality of insulating patterns 71 are formed in the circuit region 53 b, the thermal aggregation of the SOI layer 51 c of the circuit region 53 a can be inhibited, and that of the circuit region 53 b can be selectively aggregated. As a result, the plurality of the quantum dots 72 which have a silicon island structure can be formed in the circuit region 53 b using the thermal aggregation of the SOI layer 51 c. Therefore, the third preferred embodiment can integrate the SOI-FET and the single-electron memory (the quantum effect device) in the one semiconductor chip.

[0050] While the third preferred embodiment of the present invention presents an example in which the SOI-FET and the single-electron memory (the quantum effect device) are formed, simultaneously, the invention is not limited to this example, and the SOI-FET may be formed after the single-electron memory (the quantum effect device) is formed. Since an aggregation temperature of the silicon layer depends on accordance with a thickness of the silicon layer, it is necessary to control the aggregation temperature for each of various thicknesses of the silicon layer. However, in the third preferred embodiment, since the thermal aggregation of the silicon layer is used selectively, it is easy to control such a manufacturing process even where a plurality of circuit regions easy have different thicknesses. Furthermore, the third preferred embodiment can simplify a temperature setting of the manufacturing process even when plural devices require different process settings (e.g., the SOI-FET and the quantum effect device).

[0051] Further, the third preferred embodiment may be set such that a thickness of the silicon layer of the circuit region 53 b is thinner than that of the circuit region 53 a. Therefore, since the aggregation temperature of the silicon layer of the circuit region 53 b is the lower, a throughput of the manufacturing process can improve.

[0052] Further, a monocrystal silicon layer may be formed in the circuit region 53 a as a silicon layer, and an amorphous silicon layer or a poly-silicon layer may be formed in the circuit region 53 b as a silicon layer.

[0053] Further, while the third preferred embodiment of the present invention presents an example in which the quantum effect device which includes the quantum dots and quantum thin lines is formed in the silicon layer (the SOI layer), the present invention is not limited to this example and the quantum effect device may be formed in a semiconductor layer (e.g., an amorphous germanium layer and a polycrystalline germanium layer) or in a metal layer (e.g., an aluminum layer and a copper layer). The semiconductor layer and the metal layer are aggregated in condition at a temperature which is lower than the thermal aggregation temperature of the silicon layer (the SOI layer). Therefore, since the aggregation temperature at which the quantum effect device is formed is lower, the temperature setting of the manufacturing process step can be simplified.

[0054] Further, while the third preferred embodiment of the present invention presents an example in which the heat treatment is performed at a temperature of more than 800° C. in a nitride atmosphere, the present invention is not limited to this example and the heat treatment may be performed at a temperature of more than the thermal aggregation temperature of the silicon layer within a noble gas (e.g., an argon gas) atmosphere as a non-oxidizing atmosphere. As a result, a silicon nitride layer (a deposition layer) which is generated by reacting with the silicon layer (the SOI layer), due to such heat treatment at the high temperature within the nitride atmosphere, is not formed.

[0055] Further, the heat treatment may be performed at more than the thermal aggregation temperature of the silicon layer (the SOI layer) in a reducing gas atmosphere (e.g., a hydrogen gas) as a non-oxidizing atmosphere.

[0056] Further, the quantum thin line as one of the quantum effect devices may be formed so as to micro fabricate the silicon layer (the SOI layer) in a line pattern. Furthermore, a resonant tunneling device may be formed as one of the quantum effect devices.

[0057] Further, while the first thorough third embodiments of the present invention present an example which is used to form the fully depleted SOI-FET, the present invention is not limited to this example, and may be used to form various device structures, for example a double gate type device, and a thin film FET which is formed over an insulating substrate.

[0058] As described above, the method of manufacturing the semiconductor device according to the present invention can inhibit the thermal aggregation of the silicon layer (the SOI layer), since the heat treatment is performed at a temperature which is less than the aggregation temperature of the silicon layer (the SOI layer). Furthermore, since the upper surface of the silicon layer (the SOI layer) is covered with the protection layer when the heat treatment is preformed, the aggregation of the silicon layer (the SOI layer) can be inhibited. Therefore, the method of the present invention can inhibit the silicon deficiency of the silicon layer (the SOI layer).

[0059] The present invention has been described with reference to illustrative embodiments, however, this invention must not be considered to be confined only to the embodiments illustrated. Various modifications and changes of these illustrative embodiments and the other embodiments of the present invention will become apparent to those skilled in the art with reference to the description of the present invention. It is therefore contemplated that the appended claims will cover any such modifications or embodiments as fall within the true scope of the invention. 

What is claimed is:
 1. A method of manufacturing a semiconductor device comprising: providing a substrate which includes an insulating layer having an upper surface and a silicon layer extending over the upper surface of the insulating layer; forming a field insulating region in the silicon layer; forming an impurity region, which is surrounded by the field insulating region, in the silicon layer; forming a gate electrode over the silicon layer; and heat treating the silicon layer at a heat treatment temperature which is less than an aggregation temperature of the silicon layer.
 2. The method of manufacturing the semiconductor device according to claim 1, wherein T=(10t+530) ° C./nm, where T is the aggregation temperature and t is a thickness of the silicon layer.
 3. The method of manufacturing the semiconductor device according to claim 1, wherein the heat treating of the silicon layer is performed in a non-oxidizing atmosphere.
 4. The method of manufacturing the semiconductor device according to claim 3, wherein the non-oxidizing atmosphere is a noble gas atmosphere.
 5. The method of manufacturing the semiconductor device according to claim 3, wherein the non-oxidizing atmosphere is a reducing gas atmosphere.
 6. A method of manufacturing a semiconductor device comprising: providing a substrate which includes an insulating layer having an upper surface and a silicon layer extending over the upper surface of the insulating layer; forming a field insulating region in the silicon layer; forming an impurity region, which is surrounded by the field insulating region, in the silicon layer; forming a gate electrode over the silicon layer; forming a protection layer over the gate electrode and the silicon layer including the impurity region; and heat treating the silicon layer which is covered by the protection layer.
 7. The method of manufacturing the semiconductor device according to claim 6, wherein the heat treating of the silicon layer is performed at a heat treatment temperature which is equal to or more than an aggregation temperature of the silicon layer.
 8. The method of manufacturing the semiconductor device according to claim 6, wherein the heat treating of the silicon layer is performed in a non-oxidizing atmosphere.
 9. The method of manufacturing the semiconductor device according to claim 8, wherein the non-oxidizing atmosphere is a noble gas atmosphere.
 10. The method of manufacturing the semiconductor device according to claim 8, wherein the non-oxidizing atmosphere is a reducing gas atmosphere.
 11. A method of manufacturing a semiconductor device comprising: providing a substrate which includes an insulating layer having an upper surface and a silicon layer extending horizontally over the upper surface of the insulating layer; forming a field insulating region in the silicon layer; forming an impurity region, which is surrounded by the field insulating region, in the silicon layer; forming a gate electrode over the silicon layer; forming a protection layer over the gate electrode and the silicon layer including the impurity region; and heat treating the silicon layer, wherein an oxide gas is introduced during an early stage of the heat treating such that the heat treating forms an oxide layer over the gate electrode and the silicon layer including the impurity region before a temperature of the heat treating reaches an aggregation temperature of the silicon layer, and wherein the heat treating diffuses the impurity region which is covered by the oxide layer.
 12. The method of manufacturing the semiconductor device according to claim 11, wherein the diffusing of the impurity layer is performed in a non-oxidizing atmosphere.
 13. The method of manufacturing the semiconductor device according to claim 12, wherein the non-oxidizing atmosphere is a noble gas atmosphere.
 14. The method of manufacturing the semiconductor device according to claim 12, wherein the non-oxidizing atmosphere is a reducing gas atmosphere.
 15. A method of manufacturing a semiconductor device comprising: providing a substrate which includes an insulating layer having an upper surface and a silicon layer having first and second regions and extending horizontally over the upper surface of the insulating layer; forming a field insulating region in the silicon layer; forming an impurity region, which is surrounded by the field insulating layer, in the first region of the silicon layer; forming a gate electrode over the first region of the silicon layer; forming a protection layer over the gate electrode and the first region of the silicon layer including the impurity region, and an insulating pattern over the second region of the silicon layer, wherein the protection layer and the insulating pattern are formed of the same material; and forming a silicon island in the second region by heat treating of the silicon layer.
 16. The method of manufacturing the semiconductor device according to claim 15, wherein a thickness of the silicon layer of the second region is thinner than that of the first region.
 17. The method of manufacturing the semiconductor device according to claim 15, wherein the heat treating of the silicon layer is performed at a heat treatment temperature which is equal to or more than an aggregation temperature of the silicon layer.
 18. The method of manufacturing the semiconductor device according to claim 15, wherein the heat treating of the silicon layer is performed in a non-oxidizing atmosphere.
 19. The method of manufacturing the semiconductor device according to claim 18, wherein the non-oxidizing atmosphere is a noble gas atmosphere.
 20. The method of manufacturing the semiconductor device according to claim 18, wherein the non-oxidizing atmosphere is a reducing gas atmosphere.
 21. The method of manufacturing the semiconductor device according to claim 15, wherein the silicon layer at the first region is a monocrystal silicon, and the silicon layer at the second region is an amorphous silicon or a poly-silicon.
 22. The method of manufacturing the semiconductor device according to claim 21, wherein a thickness of the silicon layer at the second region is thinner than that at the first region.
 23. A method of manufacturing a semiconductor device comprising: providing a substrate which includes an insulating layer having an upper surface and a conductive layer having first and second regions and extending over the upper surface of the insulating layer, wherein the conductive layer at the first region is a silicon and the conductive layer at the second region is a semiconductor material, and wherein an aggregation temperature of the semiconductor material is lower than that of the silicon; forming a field insulating region in the conductive layer; forming an impurity region, which is surrounded by the field insulating region, in the first region of the conductive layer; forming a gate electrode over the first region of the conductive layer; forming a protection layer over the gate electrode and the first region of the conductive layer including the impurity region, and an insulating pattern over the second region of the conductive layer, and wherein the protection layer and the insulating pattern are formed of the same material; and forming a semiconductor island in the second region layer by heat treating of the conductive layer.
 24. The method of manufacturing the semiconductor device according to claim 23, wherein a thickness of the conductive layer at the second region is thinner than that of the conductive layer at the first region.
 25. The method of manufacturing the semiconductor device according to claim 23, wherein the heat treating is performed at a heat treatment temperature which is equal to or more than an aggregation temperature of the silicon.
 26. The method of manufacturing the semiconductor device according to claim 23, wherein the heat treating is performed in a non-oxidizing atmosphere.
 27. The method of manufacturing the semiconductor device according to claim 26, wherein the non-oxidizing atmosphere is a noble g as atmosphere.
 28. The method of manufacturing the semiconductor device according to claim 26, wherein the non-oxidizing atmosphere is a reducing gas atmosphere.
 29. A method of manufacturing a semiconductor device comprising: providing a substrate which includes an insulating layer having an upper surface and a conductive layer having first and second regions and extending over the upper surface of the insulating layer, wherein the conductive layer at the first region is a silicon and the conductive layer at the second region is a metal material, and wherein an aggregation temperature of the semiconductor material is lower than that of the silicon; forming a field insulating region in the conductive layer; forming an impurity region, which is surrounded by the field insulating region, in the first region of the conductive layer; forming a gate electrode over the first region of the conductive layer; forming a protection layer over the gate electrode and the first region of the conductive layer including the impurity region, and an insulating pattern over the second region of the conductive layer, and wherein the protection layer and the insulating pattern are formed of the same material; and forming a semiconductor island in the second region layer by heat treating of the conductive layer.
 30. The method of manufacturing the semiconductor device according to claim 29, wherein a thickness of the conductive layer at the second region is thinner than that of the conductive layer at the first region. 